Pale amber, free from wrinkles, air pockets, pinholes, lumps or foreign matter.
0.028 +/- 0.006 lbs/sq.ft
0.045 +/- 0.0005 inch
3.5 percent maximum
PER ASTM D903 (AL FOIL TO AL PLATE)
Peel strength (P.I.W) at 70oF +/- 5oF 10 9
Plus 7 days after 7 days aging at
70oF +/- 5oF |
10 |
9 |
Peel strength (P.I.W) 1 day at 70oF +/- 5oF
Plus 6 days at 95 to 100% relative humidity
At 120oF +/- 5oF |
15 |
14 |
Peel strength (P.I.W) 1 day at 70oF +/- 5oF 18.5 17.5
Plus 6 days exposure at 160oF +/- 5oF |
18.5 |
17.5 |
Creep distance (inches per pound/inch
of width) at 70oF +/- 5oF plus 7 days after
7 days aging at 70oF +/- 5oF. |
24 |
1.0 |
2.0 |
Creep distance (inches per pound/inch
of width) 1 day at 70oF +/- 5oF plus 6 days
at 95 to 100% relative humidity
at 120oF +/- 5oF. |
24 |
1.0 |
2.0 |
Creep distance (inches per pound/inch
of width) 1 day at 70oF +/- 5oF plus 6 days
exposure at 160oF +/- 5oF
|
24 |
0.5 |
2.0 |
BOEING BMS 5-91 TYPE II
INITIAL BOND is achieved by mounting the roll of adhesive on a rotary nip laminator and passing the adhesive film and primary substrate through the rollers with approximately 40 PSI at the nip.
is accomplished by removing the release paper from the surface of the adhesive coated primary substrate and bringing this into contact with the secondary substrate, exercising care not to entrap air between them. Use of a rotary nip laminator is recommended here, also if practicable, use of a hand roller or hand pressure is the secondary choice. Heat of approximately 150oF may be applied if necessary.
E&H CO: As manufacturer warrants that the products described and presented herein are of merchantable quality, but does not warrant their fitness for any particular use or make any other warranty, expressed or implied. Liability of E&H under this warranty is limited to replacement of the products found to be defective, or, at its option, a refund of the purchase price.
|